Fluorescent pigment Green HX 18 50 g

Fluorescent Pigment Green HX 18 For Resin Systems, Printing And Visual Production

Fluorescent Pigment Green HX 18 is a highly demanded fluorescent pigment for industrial manufacturing, decorative production and modern visual systems where extremely bright neon color and strong product visibility are essential. Today these pigments are actively used in printing industry, resin art, polymer coloring, safety marking systems, advertising materials, fishing accessories, decorative coatings, toy manufacturing, PVC products and creative handmade production. In many global markets the demand for fluorescent pigments is significantly stronger in industrial and decorative sectors than in traditional cosmetic applications.

Green fluorescent shades are especially popular in UV reactive products, airbrush art, signage systems, epoxy resin formulations, creative packaging and modern decorative manufacturing. The pigment creates an intense glow effect with impressive color depth and clean fluorescent appearance even at relatively low incorporation levels.

In cosmetic industry the component is used in decorative soap making, colorful shower gels, slime systems, bath products, artistic formulations and festival beauty products. Green fluorescent pigment is especially popular in gaming inspired cosmetics, glow collections, creative body products and trend formulations with modern visual aesthetics.

In hair care products the pigment is incorporated into temporary styling systems, decorative hair gels and visual beauty products designed to create unusual fluorescent accents. In decorative cosmetics the component helps manufacturers develop more expressive visual concepts for seasonal collections and creative beauty lines.

In SPA and wellness products fluorescent shades are used in decorative bath systems, colorful aromatic products, relaxation formulations and handmade cosmetics. Bright green fluorescent color helps formulations appear more modern and enhances the overall visual presentation of the finished product.

In industrial manufacturing the component is especially popular in resin systems, paints, coatings, inks, PVC coloring, candle decoration and polymer production. The pigment performs very well in products requiring UV visual effects, bright retail presentation and modern neon aesthetics.

The pigment is compatible with water-based systems, epoxy resin bases, transparent gels, decorative emulsions, polymer systems and glycerin formulations. It combines effectively with mica pigments, shimmer additives, pearl powders, glitter systems and transparent decorative bases. In formulations it creates rich visual texture, vivid fluorescent glow and modern sensory aesthetics.

Professional Formula For Fluorescent Resin Decor Green UV Crystal

Resin phase:
Transparent epoxy resin - 700 g
Hardener - 300 g

Decorative phase:
Fluorescent Pigment Green HX 18 - 8 g
Green pearl pigment - 2 g
Fine holographic glitter - 1.5 g

Manufacturing process:

Before production begins the epoxy resin and hardener should remain at a temperature of 22-25°C for at least 8 hours. This helps reduce resin system viscosity and minimizes the risk of air bubble formation during mixing.

In a separate container the fluorescent pigment should first be blended with a small amount of resin base until a smooth pigment dispersion is achieved without dry particles. This method helps prevent pigment clumping and provides more stable fluorescent effect distribution throughout the finished product.

After preparing the pigment dispersion the mixture should be gradually introduced into the main epoxy resin phase. Stir slowly for approximately 4-5 minutes while minimizing excessive air incorporation into the formulation.

Next the pearl pigment and holographic glitter are added. Continue gentle mixing for approximately 2 minutes at low speed in order to preserve resin transparency and maintain clean decorative visual effects.

Only after complete decorative phase distribution should the hardener be incorporated. The formulation should be mixed gently for approximately 3 minutes until full uniformity is achieved. Excessive mixing is not recommended because it may generate a large amount of trapped air bubbles.

After mixing the formulation should rest for 5-7 minutes to allow partial air release. The resin can then be slowly poured into molds using a thin stream. Remaining surface bubbles may be removed carefully with warm air if necessary.

Complete system stabilization normally occurs within 24-48 hours depending on product thickness and ambient temperature conditions.

The final product is a transparent decorative resin piece with vivid fluorescent green glow effect, impressive visual depth and modern neon aesthetics. The formulation provides stable pigment distribution, clean glass-like texture and expressive visual presentation suitable for creative manufacturing, decorative products and premium handmade collections.